设计指南:液体硅橡胶成型

金沙9999js对液态硅橡胶成型的基本指导方针包括重要的设计考虑,以帮助提高部分可塑性, 加强化妆品外观, 并减少整体生产时间.


Size

Maximum Dimensions

SIZE 12 in. x 8 in. x 4 in.
VOLUME 26 cu. in.
DEPTH No greater than 2 in. from any parting line; deeper parts are limited to a smaller outline
PROJECTED MOLD AREA 65.5 sq. in.
SIZE 304.88mm x 203.2mm x 101.6mm
VOLUME 426064 cu. mm
DEPTH No greater than 50.8mm from any parting line; deeper parts are limited to a smaller outline
PROJECTED MOLD AREA
42257.98 sq. mm

通常,金沙9999js可以保持+/- 0的加工公差.003 in. (0.08mm),线性公差±0.01 in./in. (0.01mm/mm).

清晰光学LSR医疗部分

 

 

Materials

  • 标准硅胶(30、40、50、60、70硬度计)
  • Medical-grade silicone
  • Optical-grade silicone
  • 氟硅酮(耐燃油和耐油)


VIEW MATERIALS >


Surface Finishes

FINISH DESCRIPTION
PM-F0 非化妆品,由金沙9999js自行处理

PM-F1

低修饰,大多数工具痕迹被清除

SPI-C1

600 grit stone, 10-12 Ra
PM-T1 SPI-C1 + light bead blast
PM-T2 SPI-C1 +中爆珠
SPI-A2 2级钻石buff, 1-2 Ra

Draft

VERTICAL FACES 0.5°
MOST SITUATIONS
MINIMUM FOR SHUT OFF
轻纹理最小值(pm-t1)
轻纹理最小值(pm-t2) 5°+

 

而1度的牵伸在LSR零件中是常见的, 在浅的零件上,偶尔可以容忍零牵伸. LSR的性质使得草案规则比热塑性塑料更容易被拉伸, 如果模具施工许可.

增加设计的牵伸角, even on LSR parts, 帮助方便地从模具中弹出零件, 并提高整体可塑性.

增加设计的牵伸角, even on LSR parts, 帮助方便地从模具中弹出零件, 并提高整体可塑性.


Wall Thickness

推荐的LSR成型壁厚考虑事项:

  • Walls as thin as 0.010 in. (0.254mm)是可能的,这取决于墙的尺寸和邻近较厚部分的位置.
  • 肋骨厚度应该从0.5 to 1.0乘以相邻的壁厚.
  • 内圆角的半径通常应该近似等于壁厚. 半径比这大或小得多可能导致孔隙.
适当的壁厚将减少塑料零件表面缺陷的风险.

适当的壁厚将减少塑料零件表面缺陷的风险.


Undercuts

LSR成型有能力生产具有下切的零件. 许多简单的凹口在没有机械辅助的情况下可以由压力机操作人员轻松去除. 每个部分将在一个个案的基础上审查可行性.

Undercuts, such as those shown, can complicate and, in some cases, prevent part ejection, 所以,如果可能的话,消除它们.

Undercuts, such as those shown, can complicate and, in some cases, prevent part ejection, 所以,如果可能的话,消除它们.

Radii

有些零件的角会有一个半径,而不是锋利的边缘,因为金沙9999js使用自动化数控铣削过程,使您的零件模具. 这通常不需要对模型进行更改, 但是最终的半径是在模具被磨前确定的.